Features: The rubber material has high pressure resistance, good resistance to leakage and marking, excellent resistance to pollution and aging, and excellent hydrophobicity.
Application: Organic composite insulators, lightning arresters.
Technical sheet:
| Performance | Unit | MODELNUMBER | ||
| Project | HL-3160D | HL-3160Z | HL-3160G | |
| Shore hardness | Shore A | 65±3 | 65±3 | 60±3 |
| Tear strength | KN/m | ≥10 | 12 | ≥15 |
| Tensile strength | Mpa | ≥5.5 | ≥5.5 | ≥6.0 |
| Elongation | % | ≥150 | ≥150 | ≥150 |
| Permanent set | % | ≤4 | ≤4 | ≤4 |
| Density | g/cm3 | 1.58 ± 0.03 | 1.56 ± 0.03 | 1.56 ±0.03 |
| Breakdown strength | kV/mm | 20 | 22 | 22 |
| (1AAC 4.5level) resistance to leakage and marking | mm | ≤2.5 | ≤2.5 | ≤2.5 |
| Dielectric constant | / | ≤6 | ≤6 | ≤6 |
| Volume resistivity | Ω·cm | ≥1015 | ≥1015 |
≥1015 |
● Physical data in the above table is for reference only.
● Sulfurization conditions: 175 ℃ for 5 minutes, with a liquid vulcanizing agent addition ratio of 0.65%, mainly composed of 2,5-dimethyl-2,5-di (tert butylperoxy) hexane.
●The supplied test report is obtained by the Quality Inspection Department with the curing conditions and testing method of the company; due to the difference of curing conditions and testing method, we can't guarantee that both parties obtain the same testing result, and we suggest that users should use the test data obtained under their own testing conditions as the reference for service performance. All the above performance data and application recommendations are only a reference for use on the service performance of product, instead of a guarantee on the effectiveness or general applicability of our products under a certain application.